JOHN YOUNG - SYBRON LON EXCHANGE MEMBRANE

SYBRON LON EXCHANGE MEMBRANE

Anode Membrane Plates for Electro-Coating

Premium Production
Low Permeability
Higher Total Capacity
Product Uniformity
Customized Sizes  45"W(114cm)×~50L Meters
No Waste / Continuous Roll
CMI-7000 Cation Membranes and AMI-7001 Anion Membranes

Technical  Specification

CMI-7000S CMI-7000CR AMI-7001S AMI-7001CR
Single Sheet

Continuous Roll

Single Sheet

Continuous Roll

Standard Size: US
Standard Size: Metric
48in x 124in
1.2m x 3.1m
48in x 120ft
1.2m x 37m
48in x 124in
1.2m x 3.1m
48in x 120ft
1.2m x 37m
Standard Thickness (mils) 18±1 20±1 18±1 20±1
Electrical Resistance (Ω/cm2)
0.5 mol/L NaCl
40±1 40±1 84±2 84±2
Permselectivity (%) 
0.1 mol KCl/kg / 0.5 mol KCl/kg
94 94 90 90
Total Exchange Capacity (meq/g) 1.3±1 1.3±1 1.0±1 1.0±1
Water Permeability
(ml/hr/ft2) @5psi
less than 15

less than 30

less than 15 less than 30
Mullen Burst Test strength (psi)

200

200 200 200
Thermal Stability (C°) 90 90 90 90
Chemical Stability Range (pH) 1-12 1-12 1-10 1-10
Ion Form Sodium Sodium Chloride Chloride

Preconditioning Procedure
Membranes should be preconditioned by emersion in a salt solution or a solution similar to that of the intended application for several hours to allow for membrane expansion.


JOHN YOUNG ENTERPRISE CO., LTD.

NO.5, NANYUAN RD., ZHONGLI INDUSTRIAL PARK, TAOYUAN CITY 32063, TAIWAN
TEL: 886-2-8753-4183     FAX: 886-2-8753-4185       service@john-young.com


Contact Us  |  TaiwanChina  |  Thailand  |  Singapore & Malaysia